Penyelidikan Perilaku Interaksi Kimiawi Lapisan Diamond Film Pahat Karbida Pada Operasi Bubut Kering Bahan Al 6061

  • Fransnazoan Sitorus Universitas Asahan
Keywords: Diamond-Film Coatinge of CVD Carbide Tool, Chemical Interaction dan Abrasive-Coating Wear, Dry Machining

Abstract

The purpose of the research was to characterize diamond-film coating which is used as carbide tool coating material, especially coating material (diamond-film CVD) and substrate material (WC/Co) in general approach  interaction of chemically, This is related to the research which reported about the functional failure of carbide tool coating material, used in dry machinery process of non-ferro metal in the initial wear. The study on the characteristics of tool diamond-film coating was conducted through chemical interaction approaches which occurred between the working object and tool through dry machining process. Cutting condition was v= 350 m/min; f= 0.15 mm/put; a= 1.5 mm in Initial-wear phase (tc= 1.736 min). The result of the test was abrasive wear VB = 0.070 mm.  Chemical load was tested through micro analysis using energy dispersive analysis X-Ray spectroscopy (EDAX), the result of the test was the distribution of diamond-film coating elements in aluminum 6061 testing material on the cutting conditions indicated that diamond-film coating material was still significant. The conclusion of the study was that by using chemical interaction approaches, was no coating delamination in diamond-film coating of carbide tool. The phenomenon of the three approaches was the gradual disappearing of a part of the volume of diamond-film coating material which layered substrate material as the result of abrasive-coating wear.

Downloads

Download data is not yet available.

References

[1] Jhon A.Schey, 2009, Proses Manufaktur “Introduction to Manufaktur Processes” Edisi ketiga”.

[2] Armansyah Ginting, 2004, Analisa Pembentukan Serpihan Tehadap Kegagalan dan Mekanisme Aus Pahat Karbida pada pembubutan kering Aluminium 6061-T6.

[3] Sreejith, and Ngoi, B.K.A., 2000, Dry machining, machining of the future. J.

[4] Schulz, E. Abele, A. Sahm, 2001, Material aspects of chip formation in HSC machining, Ann. CIRP 50 (1) 45–48.

[5] M. Fitzsimmons, V.K. Sarin, 2001, Surf. Coat. Technol, 158.

[6] M. Nouari, A. Ginting, 2006, Wear characteristics and performance of multi-layerCVD-coated alloyed carbide tool in dry end milling of titanium alloy.

[7] J. Hu a, Y.K. Chou, R.G. Thompson, 2008, Nanocrystalline diamond coating tools for machining high strength Al alloys.

[8] Armansyah Ginting, 2003, High Speed Machining of AISI 01 Steel With Multilayer Ceramic CVD –Coated carbide; Tool Life and Surface Integrity, Vol 14, No. 3, Agustus- majalah IPTEK.

[9] Seco. Dry Machining, (2004).

[10] Abdeel-Aal, H.M., Nouari, M., El-Mansori, M. and Ginting, A. 2006. Conceptual triboenergetic analysis of cutting tool protective coating delamination in dry cutting of hard-tocut engine alloys. Submitted to Int. J. Adv. Manuf. Technol.

[11] U.Prabhu Arumugam, Ajay P Malshe, Stephen A Batzer, Deepak G Bhat Study of Airbone Dust Emissionand Orocess Performance During Dry Machining of Aluminum-Silicon Alloy with PCD and CVD.

[12] Boothroyd, G., 1975, “Fundamentals of Metal Machining and Machine Tools, International Student Edition”, McGraw–Hill, Tokyo, Japan.

[13] Rochim T. Teori dan teknologi permesinan, HEDS, (1993)

[14] ISO 3685, “Tool-life testing with single-point turning tools”,1993.

[15] Kalpakjian, S.,“Manufacturing processes for engineering materials”, Wesley Publishing Company, USA, (2003).

[16] Sandvik Coromant, 2012, General Catalogue, (2012)., Enginering Steel.

[17] Apri Nuryanto & Sutopo, 2006, Pengaruh variasi kecepatan potong, feeding dan Kedalaman potong terhadap umur pahat hss yang dilapis aln-tin-aln.

[18] Manage, D.P., 1998, Structural and Optical Characterization of Hydrogen Amorphous Carbon Thin Films. University of Toronto: Ph.D Thesis.
Published
2017-07-28
How to Cite
[1]
F. Sitorus, “Penyelidikan Perilaku Interaksi Kimiawi Lapisan Diamond Film Pahat Karbida Pada Operasi Bubut Kering Bahan Al 6061”, JI, vol. 2, no. 1, pp. 9-18, Jul. 2017.